Direct filtration system composed of coconut fiber as a filtering medium in water treatment
DOI:
https://doi.org/10.18554/rbcti.v9i3.8180Palavras-chave:
Filter, Aluminum Sulfate, TanninResumo
The use of inorganic coagulants has sparked discussions regarding the potential consequences on human health. In contrast, polymeric coagulants derived from tannin compounds show promise in water treatment. An important issue is the use of alternative materials in the construction of filters used in water treatment, such as those made with coconut fiber. The objective of this study was to compare the performance of sand filters (F1) with coconut fiber filters (F2), as well as the use of the inorganic coagulant aluminum sulfate (C1) compared to the organic tannin (C2). The tests were performed in duplicate, and the parameters pH, electrical conductivity, apparent color, and turbidity were evaluated using R software. The results showed that the pH was not altered and that the electrical conductivity decreased after the application of both coagulants, with F2 achieving a reduction of up to 73.4% using tannin. For turbidity, F2 achieved removals of 95.44% and 81.35% for C2 and C1, respectively. When analyzing the apparent color, F2 removed 85.38% using C2 and 55.38% with C1, demonstrating the efficiency of the coconut fiber filtering material. However, the use of a large amount of water for cleaning this filter becomes a problem and an issue to be addressed.
Referências
BRANDÃO, V. A. C. A importância do tratamento adequado da água para eliminação de microorganismos. 2011. 36 p. Tese (Licenciatura em Biologia) - Universidade de Brasília, Brasília, DF, 2011.
BRASIL. Ministério da Integração e do Desenvolvimento Regional. Abastecimento de Água – 2021. Available at: https://www.gov.br/mdr/ptbr/assuntos/saneamento/snis/painel/ab. Accessed on: 2023 Sep. 06.
BRASIL. Portaria do Ministério da Saúde. Resolução nº 888, de 4 de maio de 2021. Available at: https://bvsms.saude.gov.br/bvs/saudelegis/gm/2021/prt0888_07_05_2021.html. Accessed on: 2023 Sep. 08.
CORAL, L. A.; BERGAMASCO, R.; BASSETI, F. J. Estudo da Viabilidade de utilização do polímero natural (TANFLOC) em substituição ao sulfato de alumínio no tratamento de águas para consumo. In: International Workshop advances in cleaner production. São Paulo, Brasil, 2009.
GERHARDT, C. M. Uma alternativa de substituição ao sulfato de alumínio no tratamento de água potável. 2018. 79 p. Tese (Engenharia Química Industrial) - Universidade Federal do Rio Grande do Sul, Porto Alegre, RS, 2018.
GUANINA, J. D. P. Y. Analises de la fibra de coco como filtro em el tratamiento de aguas residuales provenientes de la curtiembre moyolsa, ubicada em la parroquia pishlata de la ciudad de Ambato. 2017. 83 p. Tese (Facultad de Ingeniería Civil y Mecánica de la Carrera de Ingeniería Civil) - Universidad Técnica de Ambato, Ambato, Colômbia, 2017.
LACERDA, A. B.; BACHER, L. E.; DE OLIVEIRA, C.; ALLAGAYER, M.; RODRIGUES, M. A. S. Condutividade da Água como Indicador de Eficiência do Processo de Eletrodiálise. Inovamundi: Seminário de Pós-Graduação. Editora Feevale, v. 8, p. 4-8, 2015.
MICHELAN, D. C. De G. S. Uso de materiais não convencionais misturados com areia no meio filtrante para o tratamento de água para consumo humano. 2021. 43 p. Relatório Iniciação Científica, (Tratamento de água), Universidade Federal de Sergipe, Sergipe, SE, 2021.
NASCIMENTO, A. P.; PELEGRINI, R. T.; DE BRITO, N. N. Filtração lenta para tratamento de águas para pequenas comunidades rurais. Revista Eletrônica de Engenharia Civil, v. 2, n. 4, p. 54 - 58, 2012.
NIERO, B.; ALVES, M. V.; SKORONSKI, E. Avaliação do potencial de aplicação de tanino no tratamento de água para abastecimento captada no rio Tubarão. Revista Cadernos Acadêmicos, v. 4, n. 2, p. 188-193, 2012.
ROSALINO, M. R. R. Potenciais efeitos da presença de alumínio na água de consumo humano. 2011. 85 p. Dissertação (Mestrado em Engenharia do Ambiente) – Faculdade de Ciências e Tecnologia, Universidade Nova de Lisboa, Lisboa, 2011.
SANTOS, S. T.; LIMA, A. DE J.; MICHELAN, D. C. DE G. S. Desempenho de filtros lentos com meio filtrante de misturas de areia e materiais sustentáveis. Revista Aidis, v. 16, n. 1, p. 139-153, 2015.
SANTOS, T. M.; PEREIRA, D. F.; SANTANA, C. R.; SILVA, G. F. Estudo do tratamento físico químico da água produzida utilizando Moringa oleifera Lam em comparação ao sulfato de alumínio. Revista Exacta, v. 9, p. 317-321, 2011.
SKORONSKI, E.; NIERO, B.; FERNANDES, M.; ALVES, M. V.; TREVISAN, V. Estudo de aplicação de tanino no tratamento de água para abastecimento captada no rio Tubarão, na cidade de Tubarão SC. Revista Ambiente & Água, v. 9, n .4, p. 679-687, 2014.
THEODORO, J. D. P. Estudo dos mecanismos de coagulação/floculação para a obtenção de água de abastecimento para o consumo humano. 2012. 184 p. Tese (Doutorado Engenharia Química) - Universidade Estadual de Maringá, Maringá, PR,2012.
VIZIBELLI, D.; PEREIRA, E. R.; JANZ, F. J. L.; RIBEIRO, T.; BORGES, J. C. A. Não tecido geotêxtil agulhado aplicado como material de leito filtrante em água pré-tratada com coagulantes orgânicos. Brazilian Journal of Development, v. 5, n. 12, p. 31320-31331, 2019.
Downloads
Publicado
Como Citar
Edição
Seção
Licença
Copyright (c) 2024 Rennan Soares Ferreira, Edilaine Regina Pereira, Higor Aparecido Nunes de Oliveira, Ana Caroline Zago
Este trabalho está licenciado sob uma licença Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.